| Nee. | Harseigenskippen | Typyske wearde | Ienheid | Testmetoade |
| 1 | Spesifike swiertekrêft, 23 ℃ | 1.05 | g/cm³ | ASTM D792 |
| 2 | Skimmelkrimp, 23℃, 3.2mm, 23℃ | 0.4-0.7 | % | ASTM D955 |
| 3 | Smeltstreamsnelheid, 220 ℃, 10 kg | 22 | g/10min | ASTM D1238 |
| 4 | Treksterkte by opbringst, 23℃, 50mm/min, 3.2mm | 49 | MPa | ASTM D638 |
| 5 | Treksterkte-útwreiding by opbringst, 23 ℃, 50 mm/min, 3,2 mm | 5 | %, (Min) | ASTM D638 |
| 6 | Treksterkte by brek, 23' ℃, 50 mm/min, 3,2 mm | 10 | %, (Min) | ASTM D638 |
| 7 | Trekmodulus, 23℃, 50mm/min, 3.2mm | 2350 | MPa | ASTM D638 |
| 8 | Bûgingssterkte, 23℃, 15mm/min, 3.2mm | 78 | MPa | ASTM D790 |
| 9 | Bûgingsmodulus, 23℃, 15mm/min, 3.2mm | 2550 | MPa | ASTM D790 |
| 10 | Izod-slachsterkte, ynkerfd, 3,2 mm, 23 ℃ | 220 | J/m | ASTM D256 |
| 11 | Izod-slachsterkte, ynkerfd, 3,2 mm, -30 ℃ | 90 | J/m | ASTM D256 |
| 12 | Izod-slachsterkte, ynkerfd, 6,4 mm, 23 ℃ | 220 | J/m | ASTM D256 |
| 13 | Izod-slachsterkte, ynkerfd, 6,4 mm, -30 ℃ | 90 | J/m | ASTM D256 |
| 14 | Rockwell-hurdens, R-skaal | 110 | / | ASTM D785 |
| 15 | HDT, Edgewise, 1.82MPa, 6.4mm, Unannealed | 85 | °C | ASTM D648 |
| 16 | VICAT, 50N, 50℃/oere | 92 | °C | ASTM D1525 |
| 17 | RTI Elektrysk | 95 | °C | UL 746B |
| 18 | RTI Mechanysk mei Ynslach | 95 | °C | UL 746B |
| 19 | RTI Mechanysk sûnder ynfloed | 95 | °C | UL 746B |
| 20 | Flammberens, 1.5mm | HB | / | UL 94 |
| 21 | Flammabiliteit, 3.0mm | HB | / | UL 94 |